Abstract:
Nowadays, an area of active research in the field of clean power sources is the increase in Solid Oxide Fuel Cell efficiency. This goal can be achieved through the development of new materials for their components. In this study, two synthesis procedures were used in order to obtain cermet composites with a nickel content as high as 20 wt%. Their morphology was evidenced by Scanning Electron Microscopy (SEM). The powder prepared by direct synthesis was processed and electrochemically tested in symmetrical cells by EIS measurements under H2 atmosphere, in the temperature range 500-800ºC. A decrease in resistance with the increase in temperature was evidenced
Description:
Creșterea eficienței pilelor de combustie ceramice constituie o importantă direcție de cercetare în domeniul surselor de energie nepoluante. Acest deziderat poate fi atins prin identificarea de noi materiale pentru componentele lor. În acest studiu au fost sintetizate materiale compozite de tip cermet cu un conținut ridicat de Ni (20 % m) utilizând două metode diferite, morfologia acestora fiind evidnțiată prin microscopie electronică cu baleiaj (SEM). Pulberea obținută prin sinteză directă a fost procesată și testată electrochimic în celule simetrice, fiind efectuate măsurători de spectroscopie de impedanță electrochimică în hidrogen, în domeniul de temperatură 500-800ºC, observându-se o scădere a rezistenței odată cu creșterea temperaturii.